35-second placement time reduces risk of contamination
Moisture tolerant - works on wet or dry enamel and dentin
Uniquely suited for the "selective" etch technique
Low micro-leakage
Adhesive film thickness to be in the range of 5–10 microns
No refrigeration required. Store at 2–25 °C.
About
This Single-Bond Universal (SBU) solution offers high bond strength with one simple application technique and a quick 35-second adhesive application time. SBU can be used in all application techniques, including Total-Etch, Self-Etch and Selective-Etch. Ideal for both direct and indirect applications with virtually no post-operative sensitivity and can be used on all surfaces without any extra primer.
Combined Total-Etch, Self-Etch and Selective-Etch adhesive Consistent bond strength to both moist and dry etched dentin Virtually no post-op sensitivity. The unique chemistry of 3M™ Single Bond Universal Adhesive optimizes the ratios of the 3M proprietary 3M™ Vitrebond™ copolymer, HEMA and water. This allows for rehydration of the collagen network and formation of a distinct hybrid layer whether dentin is kept moist or dry. Flexible dispensing tip can be individually adjusted before application high bond strength to all indirect surfaces (zirconia, alumina, glass ceramics and metals) without a separate primer Excellent marginal integrity for highly esthetic restorations One-step, one-coat adhesive application Self- and dual-cure compatible with (Scotchbond™ Universal DCA Dual Cure Activator) No refrigeration needed store at room temperature for two years.
The combination of proprietary 3M™ Vitrebond™ Copolymer, HEMA and water makes the Single Bond Universal virtually no post-op sensitivity for total-etch. Unlike the several other dental adhesive those are basedon MHP, SBU contains MDP monomers of longer phosphate chain. It helps in self-etch effectiveness without refrigeration, provides greater enamel bond strength, and enables the bonding to zirconia, alumina and metal.
Applications
Adhesion of resin based composite restorative material to dentin in direct restoration
Adhesion of resin based composite restorative material to enamel in direct restoration